GC Fuji 2 LC Capsules

This innovative light-cured glass ionomer restorative in capsule form elevates the traditional properties of glass ionomers, enhancing strength, aesthetics, and ease of handling. Ideal for various restorative applications, it is designed for use in Class III and V restorations, as well as root surface caries and cervical erosion. The material's superior properties ensure optimal results even in cases of abfraction lesions, where traditional restorative materials may struggle. Additionally, it is effective for cavities with dentine margins or where proper enamel etching is not possible, making it a versatile solution for complex restorative procedures.

RECOMMENDED INDICATIONS

• Restoration of Class III , V and limited Class I
  cavities.
• Restoration of primary teeth.
• Core build up.
• Cases where a radiopaque restoration is required.
• Geriatric applications.
• As a base or liner.

CONTRAINDICATIONS

• Pulp capping.
• In rare cases the product may cause sensitivity in some people. If any such reactions are experienced,
  discontinue the use of the product and refer to a physician.

Indications:

• Class III and V restorations
• Root surface caries and cervical erosion
• Abfraction lesions
• Lesions where cavity margins are in dentine or when enamel prisms cannot be properly etched

Features: 

• Smaller particles offers excellent aesthetics and polishability
• High filler loading for significantly improved abrasion resistance
• Strontium based glass provides good radiopacity facilitating post-operative diagnosis
• Optimal adhesion to tooth structure when used in combination with GC Cavity Conditioner or GC Dentine Conditioner allowing minimal cavity preparation
• Triple cure mechanism allows for immediate finishing after light curing while ensuring total material set
• High fluoride release protects against secondary caries
• Available in VITA* shades to create natural shade match
• Faster, easier and more efficient placement
• No measuring as powder and liquid are pre-measured in the right ratio
• Mechanical mixing leads to less porosities and a stronger cement

Key Specifications: 

• Powder / Liquid Ratio (g/g) :0.33 / 0.10
• Mixing Time (sec.): 10""
• Working Time (min., sec.): 3'15""
• Light Curing Time (sec.): 20"
• Depth of Cure (A2) (mm): 1.8
• Average contents per capsule : 0.33g powder and 0.10g (0.085mL) liquid.
• Minimum net volume of mixed cement per capsule: 0.10mL."

Packaging: 

• Pack of 50

Direction To Use: 

Cavity Preparation

• Prepare tooth normally. No need for extensive retention.
• Use calcium hydroxide for pulp capping.
• Wash and gently dry (do not over-dry).
• Use GC Cavity Conditioner to remove the smear layer.

Capsule Activation & Mixing

• Shake capsule or tap to loosen powder.
• Push plunger fully to activate.
• Place in GC Capsule Applier, click once.
• Mix in amalgamator for 10 sec at high speed (~4000 RPM).

Placement

• Load into applier, click twice to prime.
• Working time: 3 min 15 sec at 23°C.
• Adjust nozzle if needed.
• Dry cavity slightly (don’t desiccate).
• Extrude cement directly (avoid air bubbles).
• Shape and apply matrix if needed.
• Light-cure for 20 sec (470 nm).
• For deep cavities (>1.8 mm), use layering.

Finishing

• Finish under water spray with fine burs, silicone points, strips.
• Apply final coating:
• GC Fuji Varnish (blow dry),
• or Fuji COAT LC (light cure 10 sec),
• or G-COAT PLUS (light cure 20 sec).